| Harta benda | unit | nilai |
| Ketumpatan Pukal | g/cm3 | 3.86 |
| Kekerasan（HV） | Gpa | >14.7 |
| Kekuatan lenturan | MPa | >=360 |
| Keliatan patah | MPa | 5-6 Mpa.m 1/2 |
| Pekali pengembangan haba | 7.0-7.5x10-6.0c | |
| Keliangan | % | <0.04% |
| Penyerapan air | % | <0.025% |
| Kekasaran permukaan | <=0.5μm | |
| Zarah saiz | Submikron |